• Efecto del voltaje de polarización sobre la resistencia a la corrosión de películas de nitruro de niobio (NbN) 

      Nieto, Jair; Caicedo, Julio Cesar; Amaya, Cesar; Aperador Chaparro, William Arnulfo; Moreno, Henry; Tirado, Liliana; Penafiel, J.A. (Colombia, 2008)
      Se depositaron películas delgadas de Nitruro de Niobio (NbN) sobre silicio (100) y substratos de acero inoxidable AISI 304 mediante un sistema multi-blanco magnetrón sputtering con r.f. (13.56 MHz), a partir de un blanco ...
    • Effect of applied bias voltage on corrosion-resistance for TiC1xNx and Ti1xNbxC1yNy coatings 

      Caicedo, Julio Cesar; Amaya, Cesar; Yate, Luis; Aperador Chaparro, William Arnulfo; Zambrano, Gustavo; Gómez , María Elena ; Muñoz Saldaña, Juan; Prieto Pulido, Pedro; Gómez De Prieto, María Elena; Gordillo Suarez, Marisol; Esguerra Arce, Johanna (ElSevierPaíses Bajos, 2010)
      Corrosion-resistance behavior of titanium carbon nitride (Ti–C–N) and titanium niobium carbon nitride (Ti–Nb–C–N) coatings deposited onto Si(1 0 0) and AISI 4140 steel substrates via r.f. magnetron sputtering process ...
    • Fracture resistant and wear corrosion performance of CrN/ZrN bilayers deposited onto AISI 420 stainless steel 

      Alba de Sánchez, Nelly Cecilia; Jaramillo, Henry E.; Vivas, Zulima; Aperador Chaparro, William Arnulfo; Caicedo, Julio Cesar; Amaya, Cesar; Jaramillo Suarez, Héctor Enrique (Suiza, 2008)
      CrN/ZrN (1, 8, 15, and 30) bilayers were deposited onto AISI 420 steel substrates at 250°C and 6.6x10-3 mbar with gas ratio Ar/N2 50:3.0 as gas mixture and bias -60V were applied. AFM analysis presented different morphologies, ...
    • Mechanical, tribological, and electrochemical behavior of Cr1xAlxN coatings deposited by r.f. reactive magnetron co-sputtering method 

      Aperador Chaparro, William Arnulfo; Caicedo, Julio Cesar; Sanchez, J.E; Sánchez, O.M; Ipaz, Leonid; Amaya, Cesar; Hernández Landaverde, M. A; Espinoza Beltrán, F. J; Muñoz Saldaña, Juan; Zambrano, Gustavo (ElSevierPaíses Bajos, 2010)
      Chromium aluminum nitride (Cr1−xAlxN) coatings were deposited onto AISI H13 steel and silicon substrates by r.f. reactive magnetron co-sputtering in (Ar/N2) gas mixture from chromium and aluminum targets. Properties of ...
    • Recubrimientos protectores basados en nitruro de niobio 

      Caicedo, Julio Cesar; Amaya, Cesar; Aperador Chaparro, William Arnulfo; Nieto, Jair; Moreno, Henry; Tirado, Liliana (Servicio de Aprendizaje - SENAColombia, 2008)
      Con el fin de encontrar alternativas que hagan frente a los problemas que ocasiona la corrosión en algunos materiales de use cotidiano son empleados en: herramientas de mecanizado, dispositivos mecánicos, moldes de inyección ...