Effect of applied bias voltage on corrosion-resistance for TiC1xNx and Ti1xNbxC1yNy coatings
(ElSevier, 2010)
Corrosion-resistance behavior of titanium carbon nitride (Ti–C–N) and titanium niobium carbon nitride
(Ti–Nb–C–N) coatings deposited onto Si(1 0 0) and AISI 4140 steel substrates via r.f. magnetron
sputtering process ...
Mechanical, tribological, and electrochemical behavior of Cr1xAlxN coatings deposited by r.f. reactive magnetron co-sputtering method
(ElSevier, 2010)
Chromium aluminum nitride (Cr1−xAlxN) coatings were deposited onto AISI H13 steel and silicon substrates by r.f. reactive magnetron co-sputtering in (Ar/N2) gas mixture from chromium and aluminum targets. Properties of ...
Efecto del voltaje de polarización sobre la resistencia a la corrosión de películas de nitruro de niobio (NbN)
(2008)
Se depositaron películas delgadas de Nitruro de Niobio (NbN) sobre silicio (100) y substratos de acero inoxidable AISI 304 mediante un sistema multi-blanco magnetrón sputtering con r.f. (13.56 MHz), a partir de un blanco ...
Fracture resistant and wear corrosion performance of CrN/ZrN bilayers deposited onto AISI 420 stainless steel
(2008)
CrN/ZrN (1, 8, 15, and 30) bilayers were deposited onto AISI 420 steel substrates at 250°C and 6.6x10-3 mbar with gas ratio Ar/N2 50:3.0 as gas mixture and bias -60V were applied. AFM analysis presented different morphologies, ...
Recubrimientos protectores basados en nitruro de niobio
(Servicio de Aprendizaje - SENA, 2008)
Con el fin de encontrar alternativas que hagan frente a los problemas que ocasiona la corrosión en algunos materiales de use cotidiano son empleados en: herramientas de mecanizado, dispositivos mecánicos, moldes de inyección ...