Corrosion Behavior of the AA2124 Aluminium Alloy Exposed to Ethanol Mixtures
Artículo de revista
2013
ESG
In the present article was studied the corrosion behavior of the AA2124 aluminum alloy which is a material used to fabricate parts of combustion engines, in a gasoline-bioethanol mixtures with concentrations of 5%, 10% and 20%. The evaluation was performed by potentiodynamics techniques and electrochemical impedance spectroscopy. It was determinate that the corrosion is more evident for mixtures with a greater amount of bioethanol and the corrosion type generated was superficial that begins on a clean surface and extends below it. En el presente artículo se estudió el comportamiento frente a la corrosión de la aleación de aluminio AA2124, que es un material utilizado para fabricar piezas de motores de combustión, en una mezcla de gasolina y bioetanol con concentraciones de 5%, 10% y 20%. La evaluación se realizó mediante técnicas de potenciodinámica y espectroscopia de impedancia electroquímica. Se determinó que la corrosión es más evidente para mezclas con mayor cantidad de bioetanol y el tipo de corrosión generada es superficial que comienza sobre una superficie limpia y se extiende por debajo de ella.
Descripción:
Artículo principal.
Título: Corrosion Behavior of the AA2124 Aluminium Alloy Exposed to.pdf
Tamaño: 509.9Kb
PDFLEER EN FLIP
Título: Corrosion Behavior of the AA2124 Aluminium Alloy Exposed to.pdf
Tamaño: 509.9Kb
PDFLEER EN FLIP