Title: Propiedades mecánicas de morteros elaborados con arena de concreto reciclado, arena de sílice y fibra de vidrio
Authors: Salgado Burgos, Ricardo Alexander 
metadata.dc.thesis.grantor: Torres Castellanos, Nancy (dr)
Keywords: Agregados reciclados
Fibra de vidrio
Arena sílice
Propiedades mecánicas
Issue Date: 2016
metadata.dc.description.resumen: El trabajo de grado de maestría en ingeniería civil con énfasis en estructuras, tuvo como finalidad evaluar el comportamiento de morteros de cemento elaborados con arena de sílice, arena obtenida de concreto reciclado, plastificante y adherente, reforzados con fibra de vidrio. Se evaluaron siete diferentes mezclas, en cinco de ellas variando el contenido de arena de sílice, arena reciclada incluyendo fibra de vidrio, en las dos restantes no se usó fibra de vidrio, las variables usadas en las mezclas fueron las siguientes (0%-100% sin fibra, 0%-100% con fibra, 25%-75%con fibra, 50%-50% con fibra, 75%-25% con fibra, 100%-0% con fibra, 100%-0% sin fibra). Todas las mezclas manejaron una relación arena: cemento de 1:1, la relación agua/cemento fue 0.4 y el contenido de fibra fue del 3.5%. Se analizaron las propiedades de resistencia a la compresión, módulo de elasticidad, flexión, velocidad de pulso ultrasónico, ISAT, porosidad, contracción, resistencia a los sulfatos, resistencia al desgaste por chorro de arena, sortividad. Los resultados de los ensayos indicaron que se obtenían mejores resistencias a la flexión cuando se tuvo una vinculación del 25% de material reciclado obteniendo mejoras del 125% respecto a las muestras patrón, en los demás ensayos realizados esta dosificación fue la de mejor comportamiento entre las mezclas con fibra y material reciclado.
Abstract: The work of magister degree in civil engineering with an emphasis on structures, aimed to evaluate the behavior of cement mortars made with silica sand, recycled concrete sand obtained, plasticizer and adhesive, reinforced with fiberglass. Seven different mixtures were evaluated in five of them varying the content of silica sand, recycled sand including fiberglass, not in the remaining two glass fiber was used, the variables used in the mixtures were the following (0% -100 % without fiber, 0% -100% fiber, 25% -75% fiber, 50% -50% fiber, 75% -25% fiber, 100% -0% fiber, 100% -0% without fiber). All blends managed a sand: cement ratio of 1: 1 water / cement ratio was 0.4 and the fiber content was 3.5%. properties compressive strength, modulus of elasticity, flexural ultrasonic pulse velocity, ISAT, porosity, shrinkage, sulfate resistance, wear resistance sandblasting, sorptivity analyzed. The test results indicated that best flexural strengths were obtained when a link 25% of material was recycled obtaining improvements of 125% compared to the standard samples in the other trials this dosage was the best performing among mixtures with fiber and recycled material.
URI: http://repositorio.escuelaing.edu.co/handle/001/469
http://catalogo-intra.escuelaing.edu.co/cgi-bin/koha/catalogue/detail.pl?biblionumber=19522
Rights: Copyright Escuela Colombiana de Ingeniería, 2016
Appears in Collections:CF - Trabajos de Grado Maestría en Ingeniería Civil

Files in This Item:
File Description SizeFormat 
CF Trabajos de Grado Maestría en Ingeniería Civil-80772270.pdfPropiedades mecánicas de morteros elaborados con arena de concreto reciclado, arena de sílice y fibra de vidrio3.38 MBAdobe PDFThumbnail
View/Open
Autorización.jpgAutorización de Publicación en Repositorio Institucional de la Escuela479.22 kBJPEGThumbnail
View/Open
Autorización.jpgAutorización de Publicación en Repositorio Institucional de la Escuela395.27 kBJPEGThumbnail
View/Open
Show full item record

Page view(s)

1
checked on Nov 9, 2017

Download(s)

11
checked on Nov 9, 2017

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.