Mechanical Performance of Concrete with Waste from Oil Industry
Artículo de revista
2016
ACI American Concrete Institute
In this paper, the mechanical properties of concrete with an added residue of the petrochemical industry (at levels of 10, 20, 30%), called catalytic cracking catalyst residue (FCC), are evaluated. The mechanical properties evaluated include compressive strength, modulus of elasticity, flexural strength, and ultrasonic pulse velocity. Two reference materials, portland cement concrete without addition and added with 20% of metakaolin (MK), were used. These tests were performed up to 360 days of curing age. Based on the results obtained, correlations were established between the different properties evaluated. The best mechanical performance was obtained with 10% FCC as a cement replacement. En este trabajo se evalúan las propiedades mecánicas del hormigón con un residuo añadido de la industria petroquímica (en niveles del 10, 20 y 30%), denominado residuo de catalizador de craqueo catalítico (FCC). Las propiedades mecánicas evaluadas incluyen la resistencia a la compresión, el módulo de elasticidad, la resistencia a la flexión y la velocidad de los impulsos ultrasónicos. Se utilizaron dos materiales de referencia, hormigón de cemento portland sin adición y adicionado con un 20% de metacaolín (MK). Estos ensayos se realizaron hasta los 360 días de edad de curado. A partir de los resultados obtenidos, se establecieron correlaciones entre las diferentes propiedades evaluadas. Las mejores prestaciones mecánicas se obtuvieron con un 10% de FCC como sustituto del cemento.
Descripción:
Mechanical Performance of Concrete with Waste from Oil Industry.pdf
Título: Mechanical Performance of Concrete with Waste from Oil Industry.pdf
Tamaño: 872.3Kb
PDF
Título: Mechanical Performance of Concrete with Waste from Oil Industry.pdf
Tamaño: 872.3Kb